10,12微米 BOPET转移膜

10,12微米 BOPET转移膜/10/12Microns thermal transfer BOPET film no corona treatment

Technical Specs. : 10 Mic PET

Sr.No.	Property	Unit	Test Method	Standards
General
1	Thickness	Micron	KME Method	10
2	Yield	M²/Kg	KME Method	71.4
3	MVTR	g/m²/24hr	38°C 90%RH	42
4	Oxygen Permeability	cc²/24hr	23°C 65% RH	100
5	Density	gm/cc	ASTM-D-1505	1.4
6	Wetting tension	Dyne/cm	ASTM D 2578	54
(Treated side)
Mechanical
1	Tensile Strength at break (MD/TD)	Kg/cm²	ASTM-D-882	1900
2	Elongation (MD/TD)	%	ASTM-D-882	90
3	Slip(COF)	--	ASTM-D-1894	0.5
Optical
1	Haze	%	ASTM-D-1003	3.5
2	Total Luminous Transmission	%	ASTM-D-1003	86
Thermal
1	Shrinkage @ 150 ° C 30min		ASTM D 1204
	MD	%		2
	TD	%		1
2	Melting Point	^oC	DSC	255
Roll
1	Width - Max	mm	KME Method	1005
2	Standard Length - Min	Mtrs	KME Method	18000
3	Standard Length - Max	Mtrs	KME Method	24000

MD - Machine Direction
TD - Transverse Direction

Technical Specs. : 12 Mic PET

Sr.No.	Property	Unit	Test Method	Standards
General
1	Thickness	Micron	KME Method	12
2	Yield	M²/Kg	KME Method	59.5
3	MVTR	g/m²/24hr	38°C 90%RH	40
4	Oxygen Permeability	cc²/24hr	23°C 65% RH	96
5	Density	gm/cc	ASTM-D-1505	1.4
6	Wetting tension	Dyne/cm	ASTM D 2578	54
(Treated side)
Mechanical
1	Tensile Strength at break (MD/TD)	Kg/cm²	ASTM-D-882	1900
2	Elongation (MD/TD)	%	ASTM-D-882	90
3	Slip(COF)	--	ASTM-D-1894	0.5
Optical
1	Haze	%	ASTM-D-1003	3.5
2	Total Luminous Transmission	%	ASTM-D-1003	86
Thermal
1	Shrinkage @ 150 ° C 30min	ASTM D 1204
MD	%	2
TD	%	1
2	Melting Point	^oC	DSC	255
Roll
1	Width - Max	mm	KME Method	1005
2	Standard Length - Min	Mtrs	KME Method	18000
3	Standard Length - Max	Mtrs	KME Method	24000
MD - Machine Direction
TD - Transverse Direction