BOPET film 6.0 microns
BOPET
film (biaxially oriented Polyester films) featurines good thermal
stability and tenacity; low air and water permeability; applicable to
vacuum aluminum plating, compound package, cooking bag manufacture,
etc.
Featuring :
Having the good adhesion with ink and coating, can be used for multi-color printings with good flatness. Is mainly used in heat-sealing bags of frozen food, industrial products and cosmetics packaging.Specification:
thickness: 12 microns-25 microns, 75 microns-150 microns ,185 microns-380 microns, 500 microns
width :200-1200MM
length : 500m ,1000m ,1500m,4000m,6000m,9000m,12000m
Polyester film is wound around paper shaft with an internal diameter of 76.2mm-152.4mm and covered with polyethylene film; each coil is supported by damper and put in carton; medium and large package needs wooden mount.
Customer's own requirement is available for us such as printed OEM logos and private label or particular size and package style.
Technical data
Number : BOPET-6.0mic
supplier | Asia Pacific Industry Group Co., Limited | commodity | BOPET | Produce number | A270 |
Address | No.3399 Luzhou Ave.,Baohe Dist., 230051, Hefei, Anhui,China | size | PETT-6.0μm | Produce date | 2018.8.01 |
tel | 0551-64687285 | item number | 39206290 | Inspect date | 2018.8.06 |
Implementation of standards | GB/T16958-2008 | quantity | Test sample volume | 100% | |
Item | Standred | Test result | Result of each items | ||
Appearance | Outliers | ≤5/m2 | satisfy | satisfy | |
Crack, relaxation, wrinkles, blemishes, impurities and defects affect the applicability of any | No obvious defects and affect the applicability | no | satisfy | ||
End surface uniformity，mm | ≤2.0 | 1 | satisfy | ||
Specifications | Width deviation，mm | ±2 | 1 | satisfy | |
Thickness deviation limit % | ±6 | -4.29 | satisfy | ||
The average thickness deviation% | ±3 | -1.14 | satisfy | ||
Physical mechanical properties | Tensile strengthMPa | Lateral | ≥170 | 258.5 | satisfy |
Longitudinal | ≥170 | 266.7 | satisfy | ||
Elongation at break% | Lateral | ≤200 | 98.9 | satisfy | |
Longitudinal | ≤200 | 99.5 | satisfy | ||
Heat shrinkage,% | Lateral | ≤3.0 | 2.36 | satisfy | |
Longitudinal | ≤3.0 | 0.06 | satisfy | ||
Modulus of elasticity,MPa | Lateral | / | 4863 | / | |
Longitudinal | / | 4560 | / | ||
Coefficient of friction | Static friction | ≤0.65 | 0.45 | satisfy | |
Dynamic friction | ≤0.55 | 0.46 | satisfy | ||
Wetting TensionmN/m | Treated surface | ≥48 | 60 | satisfy | |
Un-Treated surface | / | 43 | / | ||
Gloss,% | ≥100 | 128.9 | satisfy | ||
Haze,% | ≤8.0 | 3.43 | satisfy | ||
Transmittance,% | / | 90.5 | / | ||
Water vapor permeability（38℃，Relative humidity 0%，【g·0.1mm/(㎡·24h)】 | ≤6.6 | 3.2 | satisfy | ||
Oxygen permeability（23℃，Relative humidity 90%，【m³·cm/（c㎡·S·Pa）】 | ≤2.25×10-15 | 1.85×10-15 | satisfy | ||
Film roll joints | Shall comply with the requirements | satisfy | satisfy | ||
Health Performance | GB9685-2008& GB13113 The provisions | Shall comply with the | satisfy | satisfy | |
There should be no odor smell | No odor | No odor | satisfy | ||
Conclusions inspection | Gifted class | ||||
Remarks | |||||
Detecting people | Lin Min | Audit (stamped test chapter) | Fan Xiaowei |